- Products
- Energy Components & Materials
- IT Components & Materials
- EMC Noise Reduction Products
- Power Supply Components
- Magnetic Appliances
- Products for Flat Panel Displays
- Computers & Semiconductor IC Products
- Automotive Components & Materials
- Piping & Infrastructure Products
- Tooling, Tool Steel, Mold & Die
- Metal & Plastic Manufacturing Devices
- Aviation, Space & Nuclear Industry Materials
- Product Range Overview
Adobe® Reader® Download
The files are in Adobe Acrobat Format.
To view them you will need to download the Acrobat Reader.
The files are in Adobe Acrobat Format.
To view them you will need to download the Acrobat Reader.
Metal & Plastic Manufacturing Devices
ROLL BEARING MADE OF SIALON CERAMICS IN CONTINUOUS GALVANIZING POT
Overview
Steel materials used as continuous
submerged fusion galvanizing line materials are dissolved due to
their reaction to fusion galvanization. In particular, the shaft
and bearing portions of submerged rolls are exposed to mechanical
stress due to sliding friction, thereby showing considerable wear,
which is an impediment to improving productivity and quality. Molten
aluminum related products with excellent thermal shock resistance
have been shown to improve productivity and quality, so the use of
a structural ceramic (Sialon) for submerged roll bearings was considered.
Explanation of Product
Figure 1 is
a diagram of the continuous submerged fusion galvanizing process.
The direction of a steel plate submerged in a zinc pot at 460°C-480°C
is changed by the sink roll positioned near the central bottom portion
of the pot, and the support rolls also positioned in the pot reduce
the vibration of the plate and monitor and control its direction.
The use of sialon was considered for the bearings of support rolls and sink rolls. Figure 2 shows sialon sink roll bearings.
To prevent breakage of the sialon adapted for this purpose, a new shape was designed to prevent core slippage, interstices were installed in the bearings and standard maintenance procedures were established for re-assembly. Figure 3 shows the standard configuration for sink roll bearings when adapted for Sialon shafts.
As shown in Figure 4, practical use has shown that sialon bearings show little wear, and, due to their smoothness, there is little abrasion between these bearings and the shafts. Chart 1 shows a comparison of the average radial abrasion loss and wear and abrasion resistance of Sialon and WC-Co molten sprayed material, which is what was conventionally used. This comparison is for when conventional WC-Co molten sprayed material was used for roll shafts. As shown in Chart 1, the use of Sialon for bearings greatly increased wear and abrasion resistance. As a result of the introduction of Sialon bearings, bearing life was significantly increased, line speed was improved and A their introduction eliminates submerged bar replacement caused by bearings, increases operation days and significantly improves productivity.
Figure 1: The Continuous Submerged Fusion Galvanizing Process
The use of sialon was considered for the bearings of support rolls and sink rolls. Figure 2 shows sialon sink roll bearings.
Figure 2: Sialon Sink
Roll Bearings
To prevent breakage of the sialon adapted for this purpose, a new shape was designed to prevent core slippage, interstices were installed in the bearings and standard maintenance procedures were established for re-assembly. Figure 3 shows the standard configuration for sink roll bearings when adapted for Sialon shafts.
Figure 3: Structure of Sink Roll Bearings
As shown in Figure 4, practical use has shown that sialon bearings show little wear, and, due to their smoothness, there is little abrasion between these bearings and the shafts. Chart 1 shows a comparison of the average radial abrasion loss and wear and abrasion resistance of Sialon and WC-Co molten sprayed material, which is what was conventionally used. This comparison is for when conventional WC-Co molten sprayed material was used for roll shafts. As shown in Chart 1, the use of Sialon for bearings greatly increased wear and abrasion resistance. As a result of the introduction of Sialon bearings, bearing life was significantly increased, line speed was improved and A their introduction eliminates submerged bar replacement caused by bearings, increases operation days and significantly improves productivity.
Figure 4: View of Bearing
Following Use
Chart 1: Comparison of Wear and Abrasion Resistance
Chart 1: Comparison of Wear and Abrasion Resistance
| Average radial abrasion loss (mm per day) | Comparison of wear and abrasion resistance (thermal sprayed material/Sialon) |
||
|---|---|---|---|
| Sialon | WC-Co thermal sprayed material |
||
| Support roll bearing | 0.0005 | 0.30~0.50 | Approx. 1,000 times |
| Sink roll bearing | 0.0017 | 0.33 | Approx. 200 times |